Ideal for filling cavities where maximum strength is required at room temperature. Suitable for locking slots and bushes on shafts and housings. It has excellent holding, sealing and fastening of bolts. It is a high-strength clamping agent that makes it possible to fasten cylindrical joints, especially without cleaning.

Bottle: 15mL, 50mL and 250mL
Large volume: 1kg and 10kg

The product cures when applied between metal connections and reacts in the absence of air. Secures stud bolts, rolling bearings and roller bearings that do not require normal loosening. Particularly suitable for screw connections subjected to extreme loads. Removes backlash in worn connections. Clamps bearings in place, prevents dislocation. Clamps the rotor to the shaft. Clamps the sleeve, liners in their bearings and on the shaft.

• Resilience: High
• Viscosity Medium-High
• Colour: Green
• Appearance (uncured): Liquid
• Basic component: Methacrylate ester

• Specific gravity Conditions: 22°C: 1.04
• Flash point Method: ASTM D56-05: >93°C
• Temperature range: -50°C to +150°C
• Corrosion properties: Not corrosive
• Gap filling: up to 0.25mm
• Viscosity 4000- 4500 cPs (@20

Test method ISO 10123
Samples: Different types of pins and rings
         24 hours curing

• Specimen type: Shear strength (N/mm2)
• Steel 26 N.m
• Stainless steel 28 N.m
• Aluminium: 17 N.m
  1 week curing
• Specimen type: Shear strength (N/mm2 )
• Steel 32 N.m
• Stainless steel 30 N.m
• Aluminium: 19 N.m

The environmental resistance of the cured adhesive was measured by applying ISO 10123 preloaded assembly test at different temperatures after curing.

• Test method ISO 10123
• With pin and ring specimen: Steel
• Curing conditions and time: 22°C, 1 week
• Test conditions (except high temperature strength test): 22°C

1. Before joining the male and female parts, clean them with an absorbent cloth or wipe to thoroughly remove the cutting oil.
2. Apply the adhesive 360 degrees to the first threads of the male and female pipe fittings.
3. Wipe off excess product in the direction of the teeth with an absorbent cloth or tissue.
4. Assemble the parts and leave at 22-24°C for 24 hours to ensure complete curing.
5. To disassemble, use hand tools when separating joined parts. If disassembly at room temperature is not possible, apply localised heating to 250°C and disassemble while hot. Then mechanically remove any remaining cured adhesive and clean the parts with a suitable solvent, e.g. acetone.

Store the product in its original container at 22°C and do not expose to direct sunlight. Storage at temperatures less than 5°C and more than 30°C may adversely affect product properties. Product removed from the original container may become contaminated during use and this may affect the adhesion performance and shelf life of the product. Therefore, do not return the contaminated product to its original container. Akfa Industry does not accept responsibility for products that are contaminated or stored in a manner other than the specified storage conditions.

Shelf life 36 months at 22°C

The product contains methacrylate ester. For more detailed information, please consult the Safety Data Sheet (SDS) before use